The company operating the PA66 Taiwan's Nanya 6210GC, 6210G3, 6310,6512,6410 G3, 6410G5.6210M5, 640PG3, 640PG5, 6401G4, 6401G6; series models, such as plastic materials. The original package of products factory, quality assurance, price concessions, welcomed the new and old customers to inquire negotiate. 
 Where to buy plastic raw materials in the Company can provide material information. 

 Supply PA66 6210G9 Taiwan South Asia, the supply of PA66, 6210G9 Taiwan's Nanya wholesale supply PA66, 6210G9 Taiwan South Asia manufacturers, supply PA66, 6210G9 Taiwan's Nanya supply, supply PA66, 6210G9 Taiwan South Asia 

 Taiwan's Nanya PA66 6212G3, 15% glass fiber reinforced, enhanced toughness, Taiwan's Nanya the PA66 6212G3 wholesale, Changzhou Auspicious Plastic Co., Ltd. (Taiwan, South Asia Jiangsu distribution) Taiwan's Nanya the PA66 6212G3 use: high rigidity and high toughness at the same time require parts, base, such as skates, bicycle wheels, boxes, etc.. Taiwan's Nanya the PA66 6212G3 sales, telephone 0512 -50157780 0512 -50157781 Yi Miss 18962676501 Address: Kunshan Auspicious Plastic Co., Ltd. Kunshan City, home town of Lu Shi Tailong Plastic City, District G, on the 10th. Taiwan's Nanya the PA66 6212G3 price, Taiwan South Asia PA66, 6212G3 details. Taiwan's Nanya PA66 6212G3 engineering plastics. PA66, rubber and plastic. 

 PA66 polyamide 66 or nylon 66 
 Typical Applications: Compared with PA6, PA66, is more widely used in automotive instrument shell, and other need to have the impact resistance and high strength requirements of products. 

 Injection molding conditions: dried: If the processing of the material is sealed, then there is no need to dry. However, if the storage container is opened, it is recommended that in the 85 ° C hot air drying process. If the humidity is greater than 0.2%, also need to be 105 ° C, 12 hours of vacuum drying. Melting temperature: 260 ~ 290 ℃. Additives to the glass product is 275 ~ 280 ℃. The melting temperature should be avoided higher than 300 ℃. The mold temperature: 80 ℃ recommended. The mold temperature will affect the degree of crystallinity, degree of crystallinity will affect the physical properties of the product. For thin-walled plastic parts, use less than the mold temperature of 40C, the degree of crystallinity of the plastic parts will change over time in order to maintain the geometric stability of the plastic parts need to be annealed. Injection pressure: usually 750 ~ 1250bar, depending on material and product design. Injection speed: high speed (for enhanced material should be slightly lower). Runners and Gates: PA66, solidification time is very short, the gate location is very important. The gate aperture of not less than 0.5 × t (here t is the thickness of the plastic parts). If you use the hot runner, gate size should be smaller than the use of conventional flow, because of the hot runner can help to prevent the material from premature solidification. If sneaked into the gate, the gate of the minimum diameter should be 0.75mm. 

 Chemical and physical characteristics: PA66 polyamide material has a higher melting point. It is a semi-crystalline - crystalline materials. PA66 to maintain a strong strength and stiffness at higher temperatures. PA66 is still forming after moisture absorption, and its extent depends on the composition of the material, wall thickness, and environmental conditions. In product design, we must consider the impact of moisture absorption on the geometric stability. In order to improve the PA66, mechanical properties, often adding a variety of modifiers. Glass is the most common additives, sometimes in order to improve impact resistance, also joined the synthetic rubber such as EPDM and SBR. PA66 lower the viscosity, so liquidity is very good (but not as good as PA6). This property can be used to the processing of thin components. Its viscosity is very sensitive to temperature change. PA66 contraction rate between 1% to 2%, the glass fiber additives can be the contraction rate reduced to 0.2% to 1%. Shrinkage in the flow direction and flow direction perpendicular to the direction of differences is larger. PA66 many solvents, the anti-insoluble, resistant to weak acid and some other chlorinating agent.